Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Mold shrinkage rate | Flow | ASTM D-955 | 0.20-0.60 | % |
| density | | ASTM D-792 | 1.04 | g/cm |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile yield strength | 230℃ | ASTM D-638 | 68.5 | Mpa |
| Tensile strain at break | | ASTM D-638 | 4.0 | % |
| Rockwell hardness | | ASTM D-785 | 83 | M Scale |
| Bending modulus | 230℃ | ASTM D-790 | 3350 | Mpa |
| bending strength | 230℃ | ASTM D-790 | 93.0 | Mpa |
| IZOD notch impact strength | 23℃,3.18mm | ASTM D-256 | 14.9 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.80MPa，未退火 | ASTM D-648 | 91.1 | ℃ |
| Vicat softening temperature | Loading 1(10N) | ASTM D-1525 | 107 | ℃ |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃/5kg | ASTM D-1238 | 3.2 | g/10min |
| Melt index | 230℃/3.8kg | ASTM D-1238 | 12 | g/10min |
| Water absorption rate | 24hr | ASTM D-570 | 0.30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.