Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 横向流量 | ISO 294-4 | 2.0 | % |
| Shrinkage rate | 流量 | ISO 294-4 | 2.0 | % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 3.7 | % |
| density | | ISO 1183 | 1.18 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal tensile fracture strain | -- | ISO 527-2 | 40 | % |
| Nominal tensile fracture strain | 120°C | ISO 527-2 | > 50 | % |
| Nominal tensile fracture strain | 160°C | ISO 527-2 | > 50 | % |
| Nominal tensile fracture strain | 180°C | ISO 527-2 | > 50 | % |
| Nominal tensile fracture strain | 200°C | ISO 527-2 | > 50 | % |
| Tensile stress | 屈服 | ISO 527-2 | 100 | Mpa |
| Tensile stress | 屈服, 120°C | ISO 527-2 | 50.0 | Mpa |
| Tensile stress | 屈服, 160°C | ISO 527-2 | 40.0 | Mpa |
| Tensile stress | 屈服, 180°C | ISO 527-2 | 35.0 | Mpa |
| Tensile stress | 屈服, 200°C | ISO 527-2 | 30.0 | Mpa |
| Tensile modulus | -- | ISO 527-2 | 3300 | Mpa |
| Tensile modulus | 120°C | ISO 527-2 | 800 | Mpa |
| Tensile modulus | 160°C | ISO 527-2 | 650 | Mpa |
| Tensile modulus | 180°C | ISO 527-2 | 600 | Mpa |
| Tensile modulus | 200°C | ISO 527-2 | 500 | Mpa |
| Bending modulus | -- | ISO 178 | 3000 | Mpa |
| Bending modulus | 120°C | ISO 178 | 800 | Mpa |
| Bending modulus | 160°C | ISO 178 | 600 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 280 | °C |
| Hot deformation temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 190 | °C |
| Melting temperature 2 | | ISO 11357-3 | 295 | °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 8.5E-5 | cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 1.1E-4 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | | IEC 60243-1 | 25 | KV/mm |
| Relative permittivity | 100 Hz | IEC 60250 | 4.00 | |
| Relative permittivity | 1 MHz | IEC 60250 | 3.60 | |
| Volume resistivity | | IEC 60093 | 1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 | kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 4.0 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability level | 0.75 mm | IEC 60695-11-10, -20 | V-2 | |
| Flammability level | 1.5 mm | IEC 60695-11-10, -20 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices