Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 2781/JIS K7311 | 1.2 | |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | | ISO 868:2006(E) | 90±2/- | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| 100% tensile modulus | | ISO 37:2005(E) | 8.0 | Mpa |
| 300% tensile modulus | | ISO 37 | 17 | Mpa |
| tensile strength | | ISO 37 | 43 | Mpa |
| elongation | 断裂 | ISO 37 | 500 | % |
| tear strength | | ISP 34-1:2004(E) | 130 | kN/m |
| Rebound force | | ISO 4662 | 39 | % |
| Friction loss | | DIN 53516 | 35 | mg |
| Hardness A | | ASTM D2240/ISO 868 | 90+－2 | Shore A |
| Resilience | | ASTM D2630/ISO 4662 | 39 | % |
| 100% modulus | | ASTM D412/ISO 527 | 8 | Mpa/Psi |
| 300% modulus | | ASTM D412/ISO 527 | 17 | Mpa/Psi |
| Tensile strength | | ASTM D412/ISO 527 | 43 | Mpa/Psi |
| tear strength | | ASTM D624/ISO 34 | 130 | n/mm² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Glass transition temperature | | ASTM D3418/ISO 815 | －35 | ℃（℉） |
| vicat softening point | | ASTM D1525/ISO R306 | 115 | ℃（℉） |
| vicat softening point | | ISO 306 | 115 | °C |
| Glass transition point | | ASTM D3417 | -35 | °C |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dry conditions | | | 90℃ 2－3小时 | |
| Processing temperature | | | 155－175 | °C |
| Processing temperature | | | 185－195 | °C |
| Processing temperature | | | 185－190 | °C |
| Processing temperature | | | 190－200 | °C |
| Mold temperature | | | 20－30 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.