Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 7.0 | g/10min |
| Melt mass flow rate | 200°C/5.0kg | ISO1133 | 7.0 | g/10min |
| Density/specific gravity | | ASTMD792 | 1.04 | g/cm³ |
| Density/specific gravity | 23°C | ISO1183 | 1.04 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | 屈服,23°C | ISO527-2 | 42.0 | Mpa |
| Tensile strain | 断裂,23°C | ISO527-2 | 2.0 | % |
| Bending stress | 23°C | ISO178 | 78.0 | Mpa |
| elongation | 断裂,23°C | ASTMD638 | 2.0 | % |
| Bending modulus | 23°C | ASTMD790 | 3330 | Mpa |
| Bending modulus | 23°C | ISO178 | 3330 | Mpa |
| bending strength | 23°C | ASTMD790 | 78.0 | Mpa |
| Tensile strength | 23°C | ASTMD638 | 42.2 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTMD1525 | 94.0 | °C |
| Vicat softening temperature | | ISO306/B | 94.0 | °C |
| Hot deformation temperature 2 | 1.8MPa,Annealed,3.18mm | ASTMD648 | 87.0 | °C |
| Hot deformation temperature 2 | 1.8MPa,Annealed,3.18mm | ISO75-2/A | 87.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ISO180 | 17 | J/m |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 17 | J/m |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FlameRating | 1.5mm,NaturalColor | UL94 | HB | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| Residual Monomer | | | <700 | ppm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.