Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20to0.40 | % |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.20to0.40 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.16 | % |
| Water absorption rate | 平衡,23°C | ASTMD570 | 0.90 | % |
| Melt mass flow rate | 337°C/6.6kg | ASTMD1238 | 5.0 | g/10min |
| Density/specific gravity | | ASTMD792 | 1.51 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Strength4 | Break,100mmSpan | ASTMD790 | 228 | Mpa |
| Tensile modulus 2 | | ASTMD638 | 9310 | Mpa |
| Tensile strength 3 | 屈服 | ASTMD638 | 169 | Mpa |
| Tensile strength 3 | 断裂 | ASTMD638 | 159 | Mpa |
| Bending modulus 4 | 100mmSpan | ASTMD790 | 8960 | Mpa |
| Elongation rate 4 | 断裂 | ASTMD638 | 3.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 2E-05 | cm/cm/°C |
| Vicat softening temperature | | ASTMD15255 | 228 | °C |
| Hot deformation temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 212 | °C |
| Hot deformation temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 210 | °C |
| RTIElec | | UL746 | 180 | °C |
| Evolution Calendar intelligent importer | | UL746 | 170 | °C |
| RTIStr | | UL746 | 180 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation factor | 1kHz | ASTMD150 | 1.5E-03 | |
| Dissipation factor | 2.45GHz | ASTMD150 | 5.3E-03 | |
| Dielectric constant | 1kHz | ASTMD150 | 3.70 | |
| Volume resistivity | | ASTMD257 | 3E+16 | ohms·cm |
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 | |
| Arc resistance 6 | | ASTMD495 | PLC6 | |
| High arc combustion index | HAI | UL746 | PLC4 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 | |
| Dielectric strength | 1.60mm,inAir | ASTMD149 | 25 | KV/mm |
| Dielectric strength | 1.60mm,在油中 | ASTMD149 | 30 | KV/mm |
| Hot wire ignition | HWI | UL746 | PLC1 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| ReverseNotchIzodImpact | 3.20mm | ASTMD256 | 490 | J/m |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 85 | J/m |
| Impact strength of cantilever beam gap | 23°C | ASTMD4812 | 430 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M级 | ASTMD785 | 114 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Extreme Oxygen Index | | ASTMD2863 | 50 | % |
| UL flame retardant rating | 0.25mm | UL94 | V-0 | |
| UL flame retardant rating | 1.2mm | UL94 | 5VA | |
| NBSSmokeDensity-Flaming,Ds,4min | | ASTME662 | 1.60 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices