Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD | 内部方法 | 1.4到1.8 | % |
| Melt mass flow rate | 230°C/2.16kg | ASTMD1238 | 10 | g/10min |
| Density/specific gravity | | ASTMD1505 | 0.910 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation | 断裂 | ASTMD638 | >200 | % |
| Bending modulus | | ASTMD790 | 1670 | Mpa |
| Tensile strength | 屈服 | ASTMD638 | 32.4 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTMD1525 | 153 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 135 | °C |
| RTIElec | | UL746 | 125 | °C |
| Peak melting temperature | | ASTMD3418 | 167 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | -20°C | ASTMD256 | 29 | J/m |
| Impact strength of cantilever beam gap | 25°C | ASTMD256 | 98 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R级 | ASTMD785 | 100 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.