Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 4.5 | % |
| Shrinkage rate | TD | ISO294-4 | 0.60 | % |
| Shrinkage rate | MD | ISO294-4 | 0.20 | % |
| SpecificHeatCapacity of Melt | | | 1860 | J/kg/°C |
| ThermalConductivityofMelt | | | 0.25 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2 | 12000 | Mpa |
| Tensile stress | 断裂 | ISO527-2 | 210 | Mpa |
| Tensile strain | 断裂 | ISO527-2 | 2.4 | % |
| TensileCreepModule | 1hr | ISO899-1 | -- | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | -- | Mpa |
| Bending modulus | | ISO178 | 10300 | Mpa |
| Bending stress | | ISO178 | 300 | Mpa |
| Poisson's ratio | | ISO527 | 0.39 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 284 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 260 | °C |
| Melting temperature 2 | | ISO11357-3 | 300 | °C |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.8E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO11359-2 | 1.8E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-- | ISO11359-2 | 5.5E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO11359-2 | 5.5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | -- | ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Dielectric strength | | IEC60243-1 | 36 | KV/mm |
| Relative permittivity | 100Hz | IEC60250 | 4.00 | |
| Relative permittivity | 1MHz | IEC60250 | 4.00 | |
| Leakage Trace Index | | IEC60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 60 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 70 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M计秤 | ISO2039-2 | 108 | |
| Rockwell hardness | R计秤 | ISO2039-2 | 124 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning rate 3 | 1.00mm | ISO3795 | 23 | mm/min |
| UL flame retardant rating | 0.9mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 0.9mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| Extreme Oxygen Index | | ISO4589-2 | 24 | % |
| FMVSS flammability | | FMVSS302 | B | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| Odor | | VDA270 | 4.00 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.