PC/ABS TAIRILOY® AC2100 FCFC TAIWAN
360
- Properties:High impact resistanceThermal stabilityDimensional stability
- Usages:Electrical fieldElectronic fieldAutomotive sectorPhoneMedical devices
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | g/cm | ASTM D792,ISO 1183 | 1.16 | |
| Rockwell hardness | R-Scale | ASTM D785，ISO 2039-2 | 113 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow 3.2mm | % | ASTM D955 | 0.4－0.6 |
| Yield tensile strength | 23℃ | MPa | ASTM D638，ISO 527-2 | 52 |
| Bending modulus | 23℃ | MPa | ASTM D790，ISO 178 | 2450 |
| bending strength | 23℃ | MPa | ASTM D790 | |
| 23℃ | MPa | ISO 178 | 84 | |
| IZOD notch impact strength | 23℃,6.35mm | J/m | ISO 180，ASTM D256 | 637 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,unannealed，6.35mm | ℃ | ASTM D648 | |
| 1.8MPa,unannealed，6.35mm Span | ℃ | ISO 75-2/A | ||
| vicat softening point | ℃ | ISO 360A，ASTM 1525 | 140 | |
| Flame retardant grade | UL 94 | HB |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 240℃/5kg | g/10min | ASTM D1238，ISO 1133 | 5.5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.