Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ASTMD792 | 1.18 | g/cm³ |
| Shrinkage rate | MD2.0mm | ASTMD995 | 0.50 | % |
| Water absorption rate | (23°C,24hr) | ASTMD570 | 0.40 | % |
| Melt flow index | 260℃/2.16Kg | ASTMD1238 | 23.50 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| tensile strength | 23°C | ASTMD638 | 58.80 | Mpa |
| elongation at break | 23°C | ASTMD638 | 100 | % |
| bending strength | 23°C | ASTMD790 | 89.20 | Mpa |
| Bending modulus | 23°C | ASTMD790 | 2460 | Mpa |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 640 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.80MPa未退火 | ASTMD648 | 92.0 | °C |
| Vicat softening temperature | | ASTM1525 | 107 | °C |
| Coefficient of linear expansion | MD | ASTMD696 | 8E-05 | cm/cm/°C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | | ASTMD785 | 118 | R |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Fire rating | | UL-94 | 0.75mm | HB |
| Fire rating | | UL-94 | 0.80mm | V-2 |
| Fire rating | | UL-94 | 1.50mm | V-0 |
| Fire rating | | UL-94 | 2.00mm | V-0,5VB |
| Fire rating | | UL-94 | 3.00mm | V-0,5VB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.