Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 2.2 | g/10min |
| Melt volume flow rate | 200°C/5.0kg | ISO1133 | 2.50 | cm3/10min |
| Shrinkage rate | | ISO294-4 | 0.40to0.70 | % |
| Density/specific gravity 2 | | ASTMD792 | 1.05 | g/cm³ |
| Density/specific gravity | 23°C | ISO1183 | 1.05 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending stress 5 | | ISO178 | 82.0 | Mpa |
| Tensile strength 3 | 断裂 | ASTMD638 | 53.8 | Mpa |
| Tensile stress | 断裂 | ISO527-2/50 | 54.0 | Mpa |
| Elongation rate 4 | 断裂 | ASTMD638 | 2.0 | % |
| Tensile strain | 断裂 | ISO527-2/50 | 6.0 | % |
| Bending modulus 4 | | ASTMD790 | 3240 | Mpa |
| Bending modulus 5 | | ISO178 | 2500 | Mpa |
| Bending strength 4 | | ASTMD790 | 80.3 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,退火 | ASTMD648 | 99.0 | °C |
| Hot deformation temperature | 1.8MPa,退火 | ISO75-2/A | 99.0 | °C |
| Vicat softening temperature | | ASTMD15256 | 105 | °C |
| Vicat softening temperature | -- | ISO306/A50 | 106 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 103 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 5.0E-5to8.0E-5 | cm/cm/°C |
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 89.0 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 85.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 2.5 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 3.0 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 18 | J/m |
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTMD256 | 17 | J/m |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 1.8 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 2.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M级 | ASTMD785 | 82 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.