Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD2.0mm | ISO294-4 | 0.65 | % |
| Shrinkage rate | TD2.0mm | ISO294-4 | 0.70 | % |
| Water absorption rate | (23°C,24hr) | ISO62 | 0.30 | % |
| Water absorption rate | (23°C,50RH) | ISO62 | 0.12 | % |
| Density/specific gravity | | ISO1183 | 1.2 | g/cm³ |
| Melt flow index | 300℃/1.2Kg | ISO1133 | 19.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile creep modulus | 1Hr | ISO899-1 | 2200 | Mpa |
| Tensile creep modulus | 1000Hr | ISO899-1 | 1900 | Mpa |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 65 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 14 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 75 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 12 | kJ/m² |
| elongation at break | 23°C | ISO527-2 | >50 | % |
| Tensile modulus | 23°C | ISO527-2 | 2400 | Mpa |
| tensile strength | 23°C | ISO527-2 | 66.0 | Mpa |
| Bending modulus | 23°C | ISO178 | 2350 | Mpa |
| bending strength | 23°C | ISO178 | 98.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa未退火 | ISO75-2/Bf | 136 | °C |
| Hot deformation temperature | 1.80MPa退火 | ISO75-2/Af | 124 | °C |
| Vicat softening temperature | | ISO306/B50 | 143 | °C |
| Coefficient of linear expansion | MD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| Coefficient of linear expansion | TD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Insulation strength | | IEC60243-1 | 25 | KV/mm |
| Volume resistance | | IEC60093 | 1E+15 | Ω.cm |
| Dissipation factor | 23°C | IEC60250 | 5E-04 | 100HZ |
| Dissipation factor | 23°C | IEC60250 | 9E-03 | 1MHz |
| Dissipation factor | 相对漏电起痕指数 | IEC60112 | 250 | V |
| Dielectric constant | 23°C | IEC60250 | 3.00 | 1MHz |
| Surface resistance | | IEC60093 | 1E+16 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | | ISO2039-1 | 116 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Transmittance of 1000 μ m | | ISO13468-2 | 89.0 | % |
| Refractive index | | ISO489 | 1.58 | °C |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Fire rating | 氧指数 | ISO4589-2 | 27 | % |
| Fire rating | | UL-94 | 0.75mm | V-2 |
| Fire rating | | UL-94 | 1.50mm | V-2 |
| Fire rating | | UL-94 | 2.60mm | V-2 |
| Fire rating | | UL-94 | 2.70mm | HB |
| Fire rating | | UL-94 | 3.00mm | HB |
| Fire rating | | UL-94 | 6.00mm | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.