Technical Data Sheet
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Cantilever beam without notch impact strength | | D256 | 4.1 | J/m |
| Physical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | D792 | 0.94 | g/cm³ |
| Water absorption rate | | D570 | < 0.01 | % |
| Melt volume flow rate | 260 ℃，2.16 Kg | D1238 | 4.5 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending strength | | D790 | 58.5 | Mpa |
| Bending modulus | | D790 | 1710 | Mpa |
| Tensile strength | 屈服 | D638 | 34.9 | Mpa |
| Tensile strength | 断裂 | D638 | 41.5 | Mpa |
| Tensile strain | 断裂 | D638 | 29 | % |
| Optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Light transmittance | 3mm | | | |
| Haze | 3mm | D1003 | <0.5 | % |
| Reflection index | | | 1.51 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | 1kg, 50℃/hr | D1525 | 114.1 | °C |
| Hot deformation temperature | 0.455MPa, 2℃/min | D648 | 94.1 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.