Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Mold shrinkage rate | Flow,3.20mm | ASTM D-955 | 0.50-0.70 | % |
| density | | ASTM D-792 | 1.17 | g/cm |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending yield strength | 50.0mm Span | ASTM D-790 | 73.1 | Mpa |
| Tensile yield elongation | | ASTM D-638 | 2.1 | % |
| Tensile fracture strength | | ASTM D-638 | 35.2 | Mpa |
| IZOD notch impact strength | 23℃ | ASTM D-256 | 267 | J/m |
| Tensile modulus | | ASTM D-638 | 2410 | Mpa |
| Bending modulus | 50.0mm Span | ASTM D-790 | 2720 | Mpa |
| Tensile yield strength | | ASTM D-638 | 42.7 | Mpa |
| Tensile strain at break | | ASTM D-638 | 11 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | Flow,-40TO40℃ | ASTM E-831 | 0.000079 | cm/cm/℃ |
| Linear coefficient of thermal expansion | Transverse,-40TO40℃ | ASTM E-831 | 0.000079 | cm/cm/℃ |
| Hot deformation temperature | 0.45MPa，未退火，3.20mm | ASTM D-648 | 83.9 | ℃ |
| Hot deformation temperature | 1.80MPa，未退火，3.20mm | ASTM D-648 | 72.2 | ℃ |
| Vicat softening temperature | | ASTM D-1525 | 90.0 | ℃ |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 230℃/3.8kg | ASTM D-1238 | 6.8 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.