Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | 23℃/23℃ | ASTM D-792(ISO 1183) | 1.05 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| tensile strength | 23℃ | ASTM D-638(ISO 527) | 530(52) | kg/cm2(MPa) |
| bending strength | 23℃ | ASTM D-790(ISO 178) | 870(86) | kg/cm2(MPa) |
| flexural modulus | 23℃ | ASTM D-790(ISO 178) | 28000(2750) | kg/cm2(MPa) |
| Rockwell hardness | 23℃ | ASTM D-785(ISO 2039/2) | R-110 | |
| IZOD impact strength | 23℃ | ASTM D-256(ISO R180) | 14(137) | kg.cm/cm(J/m) |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | Unannealed 18.6kg/cm2 (1/2"厚) | ASTM D-648(ISO 75/A) | 88 | °C |
| Hot deformation temperature | Annealed (8℃×8hr) | ASTM D-648(ISO 75/A) | 100 | °C |
| vicat softening point | 1Kg load | ASTM D-1525(ISO 306) | 103 | °C |
| Combustibility | FILE NO E162823 | UL 94 | 1/16"HB All Color | |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 220℃×10kgf(98N) | ASTM D-1238(ISO 1133) | 20 | g/10min |
| Melt index | 200℃×5kgf(49N) | ASTM D-1238(ISO 1133) | 1.8 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.