Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 流动 : 1.00 mm | | 0.10 | % |
| Shrinkage rate | 横向流动 : 1.00 mm | | 0.50 | % |
| Water absorption rate | 平衡, 40°C, 95%RH | | 0.70 | % |
| Melt flow rate | 320°C/2.16 kg | ASTM D1238 | 15 | g/10 min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation | 断裂 | ASTM D638 | 4.1 | % |
| Bending modulus | | ASTM D790 | 14000 | Mpa |
| bending strength | | ASTM D790 | 270 | Mpa |
| Tensile strength | | ASTM D638 | 200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal deformation temperature under load | 1.8 MPa, 未退火 | ASTM D648 | 285 | °C |
| Melting temperature | | | 306 | °C |
| Glass transition temperature | | | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | | ASTM D149 | 30 | KV/mm |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 0 | |
| Dielectric constant | 10.0 GHz | ASTM D150 | 3.80 | |
| Volume resistivity | | ASTM D257 | 1.0E+16 | ohms·cm |
| Dissipation factor | 10.0 GHz | ASTM D150 | 0.010 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Bar Flow Length | 320°C, 500.0 µm | | 3.70 | CM |
| Weld Elongation | | ASTM D638 | 0.40 | % |
| Weld Strength | | ASTM D638 | 40.0 | Mpa |
| UL flame retardant rating | | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.