Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.34 | |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 5.7-6.3 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation at break | | ASTM D638/ISO 527 | 3/4.5 | % |
| Tensile modulus | | ASTM D638/ISO 527 | 8500/6000 | kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D638/ISO 527 | 140/100 | kg/cm²(MPa)[Lb/in²] |
| Fracture stress (V=50mm/min) | 干/湿 | | 140/100 | Mpa |
| Tensile yield stress (V=50mm/min) | 干/湿 | | 140/100 | Mpa |
| Kabi impact strength | 30℃，干 | | 60 | KJ/m |
| Bending modulus | 干/湿 | | 7100 | Mpa |
| elongation | ≤0.5%, +23℃，湿 | | 3500 | Mpa |
| Ball pressure hardness | 干/湿 | | 190 | Mpa |
| Elongation at break (V=50mm/min) | 干/湿 | | 3/4.5 | % |
| Kapi notch impact strength | +23℃，干/湿 | | 13/17 | KJ/m |
| Izo notch impact strength | +23℃，干/湿 | | 11/17 | KJ/m |
| Tensile modulus of elasticity | 干/湿 | | 8500/6000 | Mpa |
| Tensile creep modulus | 1000h,湿 | | 3500 | Mpa |
| Yield elongation (V=50mm/min) | 干/湿 | | 3/4.5 | % |
| Impact and destructive energy | +23℃，干/湿 | | 4/10 | J |
| Kabi impact strength | +23℃，干/湿 | | 65/70 | KJ/m |
| Charpy impact strength | | ASTM D256/ISO 179 | 13/17 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal conductivity | 干态 | | 0.27 | W/(m.K) |
| Temperature index | 在20000h/5000h，后拉伸强度下降50%时 | | 139/157 | °C |
| Specific heat capacity | 干态 | | 1.5 | J/(g.K) |
| Hot deformation temperature | 1.8MPa负荷，干态 | | 250 | °C |
| Hot deformation temperature | | ASTM D648/ISO 75 | 250 1.8Mpa | ℃（℉） |
| melting point | | | 260 | ℃（℉） |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 2.5-3.5/6-8 | mm/mm.℃ |
| Hot deformation temperature | 0.45MPa负荷，干态 | | 250 | °C |
| Maximum operating temperature | | | 220 | °C |
| Linear coefficient of thermal expansion | （23-80）℃，干态 | | 2.5-3.5/6-8 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | ASTM D257/IEC 60093 | 10^13/10^10 | Ω |
| Volume resistivity | | ASTM D257/IEC 60093 | 10^15/10^12 | Ω.cm |
| Relative Arc Track Index CTIM | 干/湿 | | CTI 525 M | |
| Dielectric constant | 1MHz，干/湿 | | 3.7/5 | |
| Relative arc track index CT1 | 干/湿 | | CTI 500 | |
| Dielectric strength | K20/P50，干/湿 | | 80/65 | KV/mm |
| Volume resistance | 干/湿 | | 10 | Ω.cm |
| Surface resistance | 干/湿 | | >10 | Ω |
| Loss angle | 1MHz，干/湿 | | 0.02/0.1 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.