PC/ABS TAIRILOY® AC2400 FCFC TAIWAN
230
- Properties:High mobility
- Usages:Electrical fieldElectronic fieldHousehold appliancesHousehold appliancesAutomotive sector
- Certificates:MSDS
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 3.2mm | % | ASTM D995 | 0.4－0.6 |
| Density/specific gravity | 23℃ | ISO 1183 | 1.13 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | 23℃ | R | ISO 2039/2 | |
| Bending modulus | 23℃ | MPa | ISO 178 | 2550 |
| 23℃ | Kg/cm2 | ASTM D790 | 26000 | |
| bending strength | 23℃ | Kg/cm2 | ASTM D790 | 850 |
| 23℃ | MPa | ISO 178 | 84 | |
| Tensile strength | 23℃ | MPa | ISO 527 | 49 |
| 23℃ | Kg/cm2 | ASTM D638 | 500 | |
| IZOD impact strength | 23℃ | kg.cm/cm | ASTM D785 | 55 |
| 23℃,1/8'' 厚 | J/m | ISO 180 | 539 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 18.6kg/cm2 | ℃ | ISO 75/A | 98 |
| vicat softening point | 9.8N | ℃ | ISO 306 | 122 |
| Flame retardancy | UL94 | HB | ||
| Melt index | 240℃×5Kg | g/10min | ISO 1133 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.