PA66 Zytel® ST801AHS BK010 DUPONT USA
410
- Properties:High impact resistance
- Usages:Home appliance componentsAutomotive Applications
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.4 | % |
| 流量 | ISO 294-4 | 1.8 | % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 1.1 | % |
| 饱和, 23°C, 2.00 mm | ISO 62 | 6.5 | % | |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.0 | % | |
| Stickiness number | ISO 307 | 130 | cm³/g | |
| density | ISO 1183 | 1.07 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | 50% 应变 | ISO 527-2 | 49.0 | Mpa |
| Tensile strain | 断裂 | ISO 527-2 | > 50 | % |
| Tensile creep modulus | 1 hr | ISO 899-1 | -- | Mpa |
| 1000 hr | ISO 899-1 | -- | Mpa | |
| Tensile modulus | ISO 527-2 | 2000 | Mpa | |
| Bending modulus | ISO 178 | 1800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 157 | °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 63.0 | °C | |
| Linear coefficient of thermal expansion | 流动 : 23 到 55°C | ASTM E831 | 1.4E-4 | cm/cm/°C |
| 流动 | ISO 11359-2 | 1.4E-4 | cm/cm/°C | |
| 流动 : -40 到 23°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| 流动 : 55 到 160°C | ISO 11359-2 | 1.6E-4 | cm/cm/°C | |
| 横向 : 23 到 55°C | ASTM E831 | 1.3E-4 | cm/cm/°C | |
| 横向 | ISO 11359-2 | 1.3E-4 | cm/cm/°C | |
| 横向 : -40 到 23°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| 横向 : 55 到 160°C | ISO 11359-2 | 1.3E-4 | cm/cm/°C | |
| Vicat softening temperature | ISO 306/B50 | 205 | °C | |
| Glass transition temperature 2 | ISO 11357-2 | 75.0 | °C | |
| Melting temperature 2 | ISO 11357-3 | 262 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 100 Hz | IEC 62631-2-1 | 5.0E-3 | |
| 1 MHz | IEC 62631-2-1 | 0.010 | ||
| Dielectric strength | IEC 60243-1 | 25 | KV/mm | |
| Relative permittivity | 1 MHz | IEC 62631-2-1 | 3.30 | |
| 100 Hz | IEC 62631-2-1 | 3.50 | ||
| Leakage Trace Index | IEC 60112 | 600 | V | |
| Surface resistivity | IEC 62631-3-2 | -- | ohms | |
| Volume resistivity | IEC 62631-3-1 | > 1.0E+13 | ohms·m |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Top out temperature | 190 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| Drying time - hot air dryer | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.20 | % | ||
| Processing (melt) temperature | 280 到 300 | °C | ||
| Melt Temperature, Optimum | 290 | °C | ||
| Mold temperature | 50 到 100 | °C | ||
| Mold Temperature, Optimum | 80 | °C | ||
| Maintain pressure | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 4.00 | s/mm | ||
| Maximum Screw Tangential Speed | 18 | m/min |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | -- | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 20 | kJ/m² |
| 23°C, 局部断裂 | ISO 179/1eA | 70 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 20 | kJ/m² |
| -30°C | ISO 180/1A | 15 | kJ/m² | |
| 23°C | ISO 180/1A | 80 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ISO 4589-2 | 20 | % | |
| Burning rate | 1.00 mm | ISO 3795 | < 100 | mm/min |
| UL flame retardant rating | 0.8 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | ||
| FMVSS flammability | FMVSS 302 | B |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.