Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃×5kg | ASTM D-1238 | 1.5 | g/10min |
| Melt index | 220℃×10kg | ASTM D-1238 | 16 | g/10min |
| Density/specific gravity | | ASTM D-792 | 1.06 | 23/23℃ |
| Flame retardancy | File NO.E196075 | | 1/16〃HB | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural elasticity | | ASTM D-790 | 3.9×104 | kg/cm2 |
| Tensile strength | | ASTM D-638 | 800 | kg/cm2 |
| elongation | | ASTM D-638 | 3.0 | % |
| Rockwell hardness | | ASTM D-785 | 85 | M |
| bending strength | | ASTM D-790 | 1100 | kg/cm2 |
| IZOD impact strength | 1/8" | ASTM D-256 | 2.2 | kg.cm/cm |
| IZOD impact strength | 1/4〃 | ASTM D-256 | 1.9 | kg.cm/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 未退火 | ASTM D-648 | 94(201) | ℃(°F) |
| Hot deformation temperature | 退火 | ASTM D-648 | 103(217) | ℃(°F) |
| vicat softening point | | ASTM D-1525 | 107(224) | ℃(°F) |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.