Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.91 | |
| Molding shrinkage rate | | ASTM D955 | 0.25 | % |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.05 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation at break | | ASTM D638/ISO 527 | 0.8 | % |
| tensile strength | | ASTM D638/ISO 527 | 20 | kg/cm²(MPa)[Lb/in²] |
| Bending modulus | | ASTM D790/ISO 178 | 2.5 | kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 30 | kg/cm²(MPa)[Lb/in²] |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 1.2 | kg·cm/cm(J/M)ft·lb/in |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 4.5 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Combustibility (rate) | | UL94 | V-0 | |
| Hot deformation temperature | | ASTM D648/ISO 75 | >500 | ℃（℉） |
| melting point | | | 278 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric constant | | ASTM D150/IEC 60250 | 4.0 | |
| Arc resistance | | ISO 14782 | 167 | |
| Volume resistivity | | ASTM D257/IEC 60093 | 1*10^15 | Ω.cm |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Mold temperature | | | 130-150 | °C |
| Processing temperature | | | 260-280 | °C |
| Processing temperature | | | 290-310 | °C |
| Processing temperature | | | 300-320 | °C |
| Processing temperature | | | 280-300 | °C |
| pressure | | | 40-50 | Mpa |
| pressure | | | 80-130 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.