Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 10 | g/10min |
| Melt mass flow rate | 230°C/3.8kg | ASTMD1238 | 22 | g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40到0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus 1 | | ASTMD638 | 3030 | Mpa |
| Tensile strength 2 | 屈服 | ASTMD638 | 60.7 | Mpa |
| Tensile strength 2 | 断裂 | ASTMD638 | 44.1 | Mpa |
| Elongation rate 3 | 屈服 | ASTMD638 | 3.7 | % |
| Elongation rate 3 | 断裂 | ASTMD638 | 36 | % |
| Bending modulus 4 | 50.0mm跨距 | ASTMD790 | 2550 | Mpa |
| Bending strength 5 | 屈服,50.0mm跨距 | ASTMD790 | 86.2 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 107 | °C |
| Hot deformation temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 90.0 | °C |
| Vicat softening temperature | | ASTMD15256 | 121 | °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 9E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 8.1E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 33.9 | J |
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 22.6 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R级 | ASTMD785 | 111 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Gardner glossiness | 60°,无织构 | ASTMD523 | 98 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning rate | 1.00mm | ISO3795 | 39 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.