Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 横向流量 : 4.00 mm | 内部方法 | 0.50 到 0.70 | % |
| Shrinkage rate | 流量 : 4.00 mm | 内部方法 | 0.50 到 0.70 | % |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.20 | % |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 8.00 | cm3/10min |
| density | | ISO 1183 | 1.20 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending modulus 3 | | ISO 178 | 2350 | Mpa |
| Bending stress 3 | | ISO 178 | 93.0 | Mpa |
| Tensile stress | 屈服 | ISO 527-2/50 | 61.0 | Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 | % |
| Tensile modulus | | ISO 527-2/1 | 2400 | Mpa |
| Nominal tensile fracture strain | | ISO 527-2/50 | > 50 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| Hot deformation temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 142 | °C |
| Hot deformation temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 129 | °C |
| Vicat softening temperature | | ISO 306/B50 | 149 | °C |
| RTI | 0.75 mm | UL 746 | 125 | °C |
| RTI Imp | 0.75 mm | UL 746 | 115 | °C |
| RTI Elec | 0.75 mm | UL 746 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength 4 | | IEC 60243-1 | 30 | KV/mm |
| Surface resistivity | | IEC 60093 | > 1.0E+15 | ohms |
| Volume resistivity | | IEC 60093 | > 1.0E+15 | ohms·cm |
| Relative permittivity | 100 Hz | IEC 60250 | 3.10 | |
| Relative permittivity | 1 MHz | IEC 60250 | 3.00 | |
| Leakage Trace Index | | IEC 60112 | 250 | V |
| Dissipation factor | 100 Hz | IEC 60250 | 1.0E-3 | |
| Dissipation factor | 1 MHz | IEC 60250 | 9.0E-3 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 | |
| Charpy Notched Impact Strength | | ISO 179 | 76 | kJ/m² |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| transmissivity | 3000 µm | ASTM D1003 | 88.0 | % |
| Refractive index | | ASTM D542 | 1.585 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning wire flammability index | 1.5 mm | IEC 60695-2-12 | 825 | °C |
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 875 | °C |
| Hot filament ignition temperature | 1.5 mm | IEC 60695-2-13 | 850 | °C |
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 850 | °C |
| UL flame retardant rating | 1.5 mm | UL 94 | HB | |
| UL flame retardant rating | 0.40 mm | UL 94 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.