Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ASTM D570 | 0.30 | % |
| Melt flow rate | 230°C/3.8 kg | ASTM D1238 | 1.6 | g/10 min |
| Shrinkage rate - flow | | ASTM D955 | 0.20 到 0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | 屈服 | ASTM D638 | 74.0 | Mpa |
| elongation | 断裂 | ASTM D638 | 6.0 | % |
| Bending modulus | | ASTM D790 | 3240 | Mpa |
| bending strength | | ASTM D790 | 103 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | -- | ASTM D15253 | 113 | °C |
| Vicat softening temperature | -- | ASTM D15254 | 104 | °C |
| Thermal deformation temperature under load | 0.45 MPa, 未退火 | ASTM D648 | 104 | °C |
| Thermal deformation temperature under load | 1.8 MPa, 未退火 | ASTM D648 | 98.0 | °C |
| Linear coefficient of thermal expansion - flow | | ASTM D696 | 6.5E-5 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 11 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M 级 | ASTM D785 | 97 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ASTM D542 | 1.490 | |
| transmissivity | | ASTM D1003 | 92.0 | % |
| Haze | | ASTM D1003 | 0.50 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.