Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate - flow | | ASTM D955 | 0.20 到 0.60 | % |
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 1.4 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | 屈服, 23°C | ASTM D638 | 22.1 | Mpa |
| Tensile strength | 断裂, 23°C | ASTM D638 | 27.6 | Mpa |
| elongation | 断裂, 23°C | ASTM D638 | 35 | % |
| Bending modulus | 23°C | ASTM D790 | 1170 | Mpa |
| bending strength | 屈服, 23°C | ASTM D790 | 29.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal deformation temperature under load 2 | 0.45 MPa, 退火 | ASTM D648 | 67.0 | °C |
| Thermal deformation temperature under load 2 | 1.8 MPa, 退火 | ASTM D648 | 77.0 | °C |
| Vicat softening temperature 2 | | ASTM D1525 | 87.0 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R 级, 23°C | ASTM D785 | 55 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ASTM D542 | 1.460 到 1.490 | |
| transmissivity | 1520 µm | ASTM D1003 | > 90.0 | % |
| Haze | 1520 µm | ASTM D1003 | < 8.5 | % |
| Soluble Matter Loss | 23°C | ASTM D570 | 0.10 | % |
| Weight Loss on Heating - 72 hrs | 80°C | ASTM D1562 | 1.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.