PBT VALOX™ 357X BK SABIC INNOVATIVE US
381
- Properties:Flame retardantUV resistance
- Usages:Electrical appliancesLighting fixturesHousehold goodsCharger casing
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 9.6 | g/10min |
| 265°C/5.0kg | ASTMD1238 | 13 | g/10min | |
| 266°C/5.0kg | ASTMD1238 | 13 | g/10min | |
| Shrinkage rate | MD1 | 内部方法 | 1.1到1.8 | % |
| MD:3.20mm | 内部方法 | 1.0到1.4 | % | |
| TD2 | 内部方法 | 0.90到1.8 | % | |
| Water absorption rate | 饱和,23°C | ISO62 | 0.50 | % |
| 平衡,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 8.00 | cm3/10min |
| 265°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 33.0 | mg |
| yield | ISO527-2/50 | 50.0 | Mpa | |
| ISO527-2/50 | 5.0 | % | ||
| crack | ISO527-2/50 | 40.0 | Mpa | |
| ISO527-2/50 | 30 | % | ||
| Surrender 4 | ASTMD638 | 50.0 | Mpa | |
| Fracture 5 | ASTMD638 | 40.0 | Mpa | |
| Surrender 6 | ASTMD638 | 5.0 | % | |
| Fracture 7 | ASTMD638 | 30 | % | |
| 50.0mm span 8 | ASTMD790 | 2100 | Mpa | |
| --9 | ISO178 | 2000 | Mpa | |
| --10 | ISO178 | 80.0 | Mpa | |
| Yield, 50.0mm span 11 | ASTMD790 | 78.0 | Mpa | |
| --3 | ASTMD638 | 2000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1.8MPa, unannealed, 3.20mm | ASTMD648 | 85.0 | °C | |
| 0.45MPa, unannealed, 3.20mm | ASTMD648 | 130 | °C | |
| -- | ASTMD1525,ISO306/B501322 | 145 | °C | |
| ASTMD1525,ISO306/A501423 | 180 | °C | ||
| ISO306/B120 | 150 | °C | ||
| Flow: -40 to 40 ° C | ASTME831 | 9.2E-05 | cm/cm/°C | |
| Flow: 23 to 80 ° C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 8.4E-05 | cm/cm/°C | |
| Horizontal: 23 to 80 ° C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| 0.45MPa, unannealed, 100mm span 18 | ISO75-2/Be | 135 | °C | |
| 0.45MPa, unannealed, 64.0mm span 19 | ISO75-2/Bf | 130 | °C | |
| 1.8MPa, unannealed, 100mm span 20 | ISO75-2/Ae | 85.0 | °C | |
| 1.8MPa, unannealed, 64.0mm span 21 | ISO75-2/Af | 85.0 | °C | |
| thermal conductivity | ISO8302 | 0.17 | W/m/K | |
| RTI | UL746 | 140 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| RTIElec | UL746 | 120 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257,IEC60093 | >1.0E+15 | ohms·cm | |
| Leakage Trace Index | -- | IEC60112 | 225 | V |
| 解决方案B | IEC60112 | 100 | V | |
| 1MHz | IEC60250 | 1.3E-03 | ||
| ASTMD150,IEC60250 | 3.00 | |||
| ASTMD150 | 0.013 | |||
| Hot wire ignition | HWI | UL746 | PLC3 | |
| 50Hz | IEC60250 | 3.00 | ||
| IEC60250 | 2E-03 | |||
| 60Hz | IEC60250 | 2E-03 | ||
| IEC60250 | 3.00 | |||
| Arc resistance 24 | ASTMD495 | PLC6 | ||
| 1.60mm,inOil | ASTMD149 | 25 | KV/mm | |
| 3.20mm, inoil | ASTMD149 | 17 | KV/mm | |
| 0.800mm, in oil | IEC60243-1 | 34 | KV/mm | |
| 1.60mm, in oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm, in oil | IEC60243-1 | 17 | KV/mm | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 | |
| High arc combustion index | HAI | UL746 | PLC0 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C,1500sec^-1 | ISO11443 | 310 | Pa·s |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam without notch impact strength | -30°C | ASTMD4812,ISO180/1U | 无断裂 | |
| 23°C | ASTMD4812,ISO180/1U | 无断裂 | ||
| 23°C | ASTMD256 | 500 | J/m | |
| ISO179/2C | 40 | kJ/m² | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 35.0 | J |
| -30°C12 | ISO179/1eA,ISO179/2C | 20 | kJ/m² | |
| 23°C13 | ISO179/1eA | 45 | kJ/m² | |
| Simply supported beam without notch impact strength 14 | -30°C | ISO179/1eU,ISO179/2U | 无断裂 | |
| 23°C | ISO179/1eU,ISO179/2U | 无断裂 | ||
| -30°C | ASTMD256 | 150 | J/m | |
| 0°C | ASTMD256 | 190 | J/m | |
| -30°C15 | ISO180/1A | 10 | kJ/m² | |
| 0°C16 | ISO180/1A | 20 | kJ/m² | |
| 23°C17 | ISO180/1A | 40 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R计秤 | ISO2039-2 | 115 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 115 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ISO4589-2 | 30 | % | |
| UL flame retardant rating | 0.750mm | UL94 | V-0 | |
| 2.50mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.00mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.