Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 1.00 | cm3/10min |
| Melt volume flow rate | 230°C/2.16kg | ISO1133 | 6.00 | cm3/10min |
| Water absorption rate | 饱和,23°C | ISO62 | 0.010 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2/1A/1000 | 2600 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Glass transition temperature 3 | | ISO11357-2 | 65.0 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | MD | ISO527-3 | 1700 | Mpa |
| Tensile modulus | TD | ISO527-3 | 2000 | Mpa |
| Tensile stress | MD:断裂 | ISO527-3 | 55.0 | Mpa |
| Tensile stress | TD:断裂 | ISO527-3 | 55.0 | Mpa |
| elongation | MD:断裂 | ISO527-3 | 2.9 | % |
| elongation | TD:断裂 | ISO527-3 | 3.6 | % |
| Falling hammer impact | | ISO7765-1 | <36 | g |
| Elmondov tear strength | MD | ISO6383-2 | 2.3 | N |
| Elmondov tear strength | TD | ISO6383-2 | 2.4 | N |
| Oxygen permeability rate | 23°C,50%RH | ASTMD3985 | 17 | cm³·mm/m²/atm/24hr |
| WaterVaporPermeability2 | 38°C | ISO15106-3 | 0.800 | g·100µm/(m²·day |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| gloss | 60° | ISO2813 | >100 | |
| Haze | | ISO14782 | <1.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.