Technical Data Sheet
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | | 12000 | Mpa |
| Charpy notch impact strength | 23℃ | | 4 | KJ/m |
| Tensile fracture strength | | | 110 | Mpa |
| Tensile fracture elongation | | | 2 | % |
| Tensile elongation modulus | 1h | | 9500 | Mpa |
| Tensile elongation modulus | 1000h | | 7500 | Mpa |
| Charpy impact strength | 23℃ | | 17 | KJ/m |
| Charpy impact strength | -30℃ | | 17 | KJ/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.80MPa | | 105 | °C |
| Hot deformation temperature | 0.45MPa | | 108 | °C |
| vicat softening point | 50℃/H50n | | 109 | °C |
| Linear expansion coefficient | 平行方向 | | 0.25 | E-4/℃ |
| Combustibility | 1.6mm | UL 94 | HB | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation factor | 100Hz | | 70 | E-4 |
| Dissipation factor | 1MHz | | 100 | E-4 |
| Relative Arc Track Mathematics CTI | | | 600 | |
| Surface resistivity | | | >1E15 | Ω |
| Dielectric constant | 100Hz | | 3.5 | |
| Dielectric constant | 1MHz | | 3.2 | |
| Volume resistivity | | | >1E13 | Ω.m |
| Dielectric strength | | | 39 | KV/mm |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen index | | | 20 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | | | 0.25 | % |
| Density/specific gravity | | | 1360 | kg/m |
| Melt index | 220℃/10kg | | 5 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.