ASA/PC GELOY™ XP4034-WH5E117 SABIC INNOVATIVE US
640
- Properties:High mobilityThermal stabilityAntistaticWeather resistance
- Usages:Automotive sector
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 220°C/10.0 kg | ASTM D1238 | 5.0 | g/10 min |
| 260°C/5.0 kg | ASTM D1238 | 14 | g/10 min | |
| 280°C/3.8 kg | ASTM D1238 | 24 | g/10 min | |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| 横向流动 : 3.20 mm | 内部方法 | 0.50 到 0.70 | % | |
| Water absorption rate | 24 hr | ASTM D570 | 0.25 | % |
| Outdoor applicability | UL 746C | f2 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2500 | Mpa | |
| Tensile strength | 屈服 2 | ASTM D638 | 62.0 | Mpa |
| 屈服 | ISO 527-2/50 | 57.0 | Mpa | |
| 断裂 | ISO 527-2/50 | 50.0 | Mpa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.5 | % |
| 断裂 2 | ASTM D638 | 25 | % | |
| 断裂 | ISO 527-2/50 | 130 | % | |
| Bending modulus | 50.0 mm 跨距 3 | ASTM D790 | 2510 | Mpa |
| -- 4 | ISO 178 | 2500 | Mpa | |
| Bending stress | -- 4, 5 | ISO 178 | 75.0 | Mpa |
| 屈服, 50.0 mm 跨距 3 | ASTM D790 | 88.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 115 | °C |
| 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Bf | 116 | °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 104 | °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Af | 98.0 | °C | |
| Vicat softening temperature | ISO 306/B50 | 113 | °C | |
| Linear coefficient of thermal expansion | 流动 : -20 到 150°C | ASTM E831 | 7.2E-5 | cm/cm/°C |
| 横向 : -20 到 150°C | ASTM E831 | 7.2E-5 | cm/cm/°C | |
| thermal conductivity | ASTM C177 | 0.25 | W/m/K |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 95 到 105 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.040 | % | ||
| Suggested injection volume | 40 到 80 | % | ||
| Temperature at the rear of the barrel | 240 到 255 | °C | ||
| Temperature in the middle of the barrel | 245 到 260 | °C | ||
| Temperature at the front of the material cylinder | 250 到 265 | °C | ||
| Spray nozzle temperature | 245 到 265 | °C | ||
| Processing (melt) temperature | 260 到 275 | °C | ||
| Mold temperature | 55 到 70 | °C | ||
| Back pressure | 0.300 到 1.00 | Mpa | ||
| Screw speed | 30 到 80 | rpm | ||
| Exhaust hole depth | 0.038 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | -30°C, Total Energy | ASTM D3763 | 30.0 | J |
| 23°C, Total Energy | ASTM D3763 | 47.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 110 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Gardner glossiness | 60°, 无织构 | ASTM D523 | 94 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.