Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Cutting thickness | | FPC方法 | 优 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Mold expansion ratio | DSR | FPC方法 | 1.75 | % |
| Tensile elongation at break | | ASTM D-638 | 800 | % |
| ESCR | | ASTM D-1693 | >1000 | hours |
| Aishi notch impact strength | | ASTM D-256 | NB | kg·cm/cm |
| Resistance to impact strength | | ASTM D-1822 | 1000 | kg/cm2 |
| hardness | | ASTM D-2240 | 67 | Shore D |
| Tensile fracture strength | | ASTM D-638 | 380 | kg/cm2 |
| Tensile strength reduction | | ASTM D-638 | 270 | kg/cm2 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| softening point | | ASTM D-1525 | 127 | °C |
| Brittle temperature | | ASTM D-746 | <-70 | °C |
| melting point | | FPC方法 | 134 | °C |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ASTM D-1505 | 0.953 | g/cm³ |
| Melt index | MI5/MI21.6 | ASTM D-1238 | 0.10/2.5 | g/10min |
| Melt index | MI2.16 | ASTM D-1238 | 0.02 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.