Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ISO1183 | 1.25 | g/cm³ |
| Shrinkage rate | | | 0.60到1.0 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 1.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2 | 6800 | Mpa |
| Tensile stress | 屈服 | ISO527-2 | 125 | Mpa |
| Tensile stress | 断裂 | ISO527-2 | 125 | Mpa |
| Tensile strain | 屈服 | ISO527-2 | 4.5 | % |
| Tensile strain | 断裂 | ISO527-2 | 4.5 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 240 | °C |
| Hot deformation temperature | 连续使用温度2 | | 110 | °C |
| Vicat softening temperature | | ISO306/A120 | 255 | °C |
| BallPressure Test | 165°C | IEC60695-10-2 | 通过 | |
| Melting temperature | | DSC | 260 | °C |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 250 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Leakage Trace Index | | IEC60112 | 500 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | | ISO180/A | 7.5 | kJ/m² |
| Unscented Izod impact strength | | ISO180 | 40 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| UL flame retardant rating | 3.2mm | UL94 | HB | |
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 650 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.