Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | 23°C | ISO1183 | 1.24 | g/cm³ |
| Melt volume flow rate | 270°C/5.0kg | ISO1133 | 49.0 | cm3/10min |
| Shrinkage rate | TD1 | ISO2577 | 0.65 | % |
| Shrinkage rate | TD:90°C,1小时 | ISO2577 | 0.10 | % |
| Shrinkage rate | MD2 | ISO2577 | 0.65 | % |
| Shrinkage rate | MD:90°C,1小时 | ISO2577 | 0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 23°C | ISO527-2/1 | 2600 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2/50 | 70.0 | Mpa |
| Tensile stress | 断裂,23°C | ISO527-2/50 | 54.0 | Mpa |
| Tensile strain | 屈服,23°C | ISO527-2/50 | 5.5 | % |
| Tensile strain | 断裂,23°C | ISO527-2/50 | 110 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| 0.45MPa, unannealed | | ISO75-2/B | 128 | °C |
| 1.8MPa, unannealed | | ISO75-2/A | 108 | °C |
| Vicat softening temperature | | ISO306/B120 | 140 | °C |
| RTIElec | | UL746 | 75.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 75.0 | °C |
| RTI | | UL746 | 75.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 6.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 8.0 | kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 无断裂 | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 无断裂 | |
| Impact strength of cantilever beam gap | -30°C | ISO180/A | 6.0 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/A | 7.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.50mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.