Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.05 | |
| Molding shrinkage rate | | ASTM D955 | 0.4-0.6 | % |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 1.5 | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 23℃(73℉) | ASTM D-955 | 0.4-0.6 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | 23℃(73℉) | ASTM D-638 | 460 | Kgf/cm2 |
| impact strength | 1/4〃(6.35mm) 23℃(73℉) | ASTM D-256 | 18 | Kgf.cm/cm |
| Flexural modulus | 23℃(73℉) | ASTM D-790 | 2450 | Kgf/cm2 |
| Rockwell hardness | 23℃(73℉) | ASTM D-785 | 105 | M Scale |
| Flexural strength | 23℃(73℉) | ASTM D-790 | 735 | Kgf/cm2 |
| tensile strength | | ASTM D638/ISO 527 | 470 | kg/cm²(MPa)[Lb/in²] |
| Rockwell hardness | | ASTM D785 | R-110 | |
| Bending modulus | | ASTM D790/ISO 178 | 780 | kg/cm²(MPa)[Lb/in²] |
| Charpy impact strength | | ASTM D256/ISO 179 | 22 | kg·cm/cm(J/M)ft·lb/in |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 20 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | | ASTM D648/ISO 75 | 87 | ℃（℉） |
| Hot deformation temperature | 18.6kgf/cm2(264 Psi) | ASTM D-648 | 87 | °C |
| Hot deformation temperature | 18.6kgf/cm2(264 Psi) | ASTM D-648 | 189 | ℉ |
| Combustibility | FILE NO.E206417(1.59mm) | UL-94 | 1/16"HB | |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃ 5000g | ASTM D-1238 | 1.6 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.