Technical Data Sheet
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation | 断裂 | ASTM D-638 | ＞250 | % |
| elongation | 断裂 | ASTM D-638 | ＞250 | % |
| Rockwell hardness | 23℃ | ASTM D-785 | 100 | R scale |
| Bending modulus | | ASTM D-790 | 17000 | kg/cm2 |
| Tensile strength | 50mm/min | ASTM D-638 | 380 | kg/cm2 |
| Tensile strength | 50mm/min | ASTM D-638 | 380 | kg/cm2 |
| Tensile strength (fracture) | 50mm/min | ASTM D-638 | 200 | kg/cm2 |
| IZOD impact strength | 1/4"，23℃ | ASTM D-256 | 3 | kg.cm/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | 1kg | ASTM D-1525 | 155 | ℃ |
| Hot deformation temperature | 18.6kg/cm2(1/8") | ASTM D-648 | 65 | ℃ |
| Hot deformation temperature | 4.6kg/cm2(1/8") | ASTM D-648 | 110 | ℃ |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 230℃，2.16kg | ASTM D-1238 | 22 | g/10min |
| Melt index | 230℃，2.16kg | ASTM D-1238 | 22 | g/10min |
| density | | ASTM D-1505 | 0.91 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.