Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.2 | |
| Molding shrinkage rate | | ASTM D955 | 0.002-0.005 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation at break | | ASTM D412/ISO 527 | 54 | % |
| Tensile modulus | | ASTM D412/ISO 527 | 1800 | kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D412/ISO 527 | 44 | kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D412/ISO 527 | 47 | % |
| Rockwell hardness | | ASTM D785 | 105 | kg·cm/cm(J/M)ft·lb/in |
| Bending modulus | | ASTM D790/ISO 178 | 1850 | kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 1800 | kg/cm²(MPa)[Lb/in²] |
| IZOD notch impact strength | | ASTM D256/ISO 179 | NB | kg·cm/cm(J/M)ft·lb/in |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 77 | kg/cm²(MPa)[Lb/in²] |
| Charpy impact strength | | ASTM D256/ISO 179 | 7.8 | kg·cm/cm(J/M)ft·lb/in |
| Charpy impact strength | | ASTM D256/ISO 179 | NB | kg·cm/cm(J/M)ft·lb/in |
| Charpy impact strength | | ASTM D256/ISO 179 | 4.8 | kg·cm/cm(J/M)ft·lb/in |
| Tensile elongation at break (elongation at break) | | ASTM D412/ISO 527 | 46 | kg/cm²(MPa)[Lb/in²] |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Fuzzy coefficient (Haze) | | ISO 14782 | 0.3 | % |
| Light transmittance | | ASTM D1003/ISO 13468 | 89 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.