Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | | ISO294-4 | 0.40到0.70 | % |
| Melt mass flow rate | 220°C/10.0kg | ISO1133 | 30 | g/10min |
| Density/specific gravity | 23°C | ISO1183 | 1.04 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending modulus 3 | | ISO178 | 2000 | Mpa |
| Bending stress 3 | | ISO178 | 61.0 | Mpa |
| Tensile stress | 屈服 | ISO527-2/50 | 40.0 | Mpa |
| Tensile stress | 断裂 | ISO527-2/50 | 31.0 | Mpa |
| Tensile strain | 断裂 | ISO527-2/50 | 40 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 8.6E-05 | cm/cm/°C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 83.0 | °C |
| Hot deformation temperature | 1.8MPa,退火 | ISO75-2/A | 98.0 | °C |
| Vicat softening temperature | -- | ISO306/A50 | 105 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 101 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179 | 29 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 27 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.