Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD | ASTMD995 | 0.046 | % |
| Shrinkage rate | 堆积密度 | ASTMD4894 | 0.36 | g/cm³ |
| Shrinkage rate | MIT弯曲的寿命 | ASTMD2178 | 2.7E+07 | |
| Shrinkage rate | 拉伸空隙指数 | ASTMD4895 | 40.0 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation at break | 23°C | ASTMD638 | 430 | % |
| elongation at break | 抗压强度 | ASTMD695 | 7.7 | Mpa |
| elongation at break | 抗压强度 | ASTMD695 | 4.7 | Mpa |
| elongation at break | 抗压强度 | ASTMD695 | 28.3 | Mpa |
| elongation at break | 受载变形 | ASTMD621 | 12.9 | % |
| elongation at break | 受载变形 | ASTMD621 | 24.9 | % |
| elongation at break | 受载变形 | ASTMD621 | 17.7 | % |
| elongation at break | 压缩形变 | ASTMD621 | 4.8 | % |
| elongation at break | 压缩形变 | ASTMD621 | 8.7 | % |
| elongation at break | 压缩形变 | ASTMD621 | 5.0 | % |
| tensile strength | 23°C | ASTMD638 | 40 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | 熔融温度 | DSC | 323 | °C |
| Vicat softening temperature | 连续使用温度 | | 260 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric constant | | ASTMD150 | <2.10 | 1kHz |
| Dissipation factor | | ASTMD150 | <1.0E-4 | |
| Insulation strength | | ASTMD149 | 3300 | KV/mm |
| Volume resistance | | ASTMD257 | >1.0E+18 | Ω.cm |
| Surface resistance | | ASTMD257 | >1.0E+15 | Ω.cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.