Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：3.20mm | | 0.20 | % |
| Shrinkage rate | TD：3.20mm | | 0.40 | % |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.020 | % |
| Density/specific gravity | | ASTMD792 | 1.99 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | | ASTMD638 | 124 | Mpa |
| Bending stress | | ISO178 | 210 | Mpa |
| compressive strength | | ASTMD695 | 265 | Mpa |
| Poisson's ratio | | ISO527 | 0.36 | |
| Tensile stress | | ISO527-2 | 135 | Mpa |
| Tensile strain | 断裂 | ISO527-2 | 0.80 | % |
| elongation | 断裂 | ASTMD638 | 0.90 | % |
| Bending modulus | | ASTMD790 | 19300 | Mpa |
| Bending modulus | | ISO178 | 19000 | Mpa |
| bending strength | | ASTMD790 | 207 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 265 | °C |
| Linear coefficient of thermal expansion | TD：100到200°C | ASTME831 | 7E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：导热系数 | ASTME831 | 0.59 | W/m/K |
| Linear coefficient of thermal expansion | MD：-50到50°C | ASTME831 | 1.5E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | MD：100到200°C | ASTME831 | 1.5E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-50到50°C | ASTME831 | 3E-05 | cm/cm/°C |
| UL temperature rating | | UL746B | 220to240 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| InsulationResistance2 | 90°C | | 1E+11 | ohms |
| Compared to the anti leakage trace index | CTI | UL746 | 250 | V |
| Dielectric strength | | ASTMD149 | 16 | KV/mm |
| Dissipation factor | 25°C,1kHz | ASTMD150 | 4E-03 | |
| Dissipation factor | 25°C,1MHz | ASTMD150 | 2E-03 | |
| Surface resistivity | | ASTMD257 | 1E+16 | ohms |
| Dielectric constant | 25°C,1kHz | ASTMD150 | 4.90 | |
| Dielectric constant | 25°C,1MHz | ASTMD150 | 4.90 | |
| Arc resistance | | ASTMD495 | 185 | sec |
| Volume resistivity | | ASTMD257 | 1E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Unscented Izod impact strength | | ISO180 | 15 | kJ/m² |
| Cantilever beam without notch impact strength | 3.18mm | ASTMD4812 | 210 | J/m |
| Impact strength of cantilever beam gap | 3.17mm | ASTMD256 | 53 | J/m |
| Impact strength of cantilever beam gap | | ISO180/A | 6.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M计秤 | ASTMD785 | 101 | |
| Rockwell hardness | R计秤 | ASTMD785 | 118 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FlameRating | 1.6mm | UL94 | V-05VA | |
| Extreme Oxygen Index | | ASTMD2863 | 61 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.