Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.20to0.50 | % |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.13 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.13 | % |
| Density/specific gravity | | ASTMD792 | 1.23 | g/cm³ |
| Density/specific gravity | 23°C | ISO1183 | 1.23 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | 断裂,23°C | ASTMD638 | 52.0 | Mpa |
| Tensile strength | 屈服,23°C | ASTMD638 | 45.0 | Mpa |
| TensileStrain | Break,23°C,4.00mm | ISO527-2 | 230 | % |
| TensileStrain | Yield,23°C,4.00mm | ISO527-2 | 4.4 | % |
| Tensile modulus | 23°C | ASTMD638 | 1800 | Mpa |
| tensile strength | Yield,23°C,4.00mm | ISO527-2 | 46.0 | Mpa |
| tensile strength | Break,23°C,4.00mm | ISO527-2 | 47.0 | Mpa |
| elongation | 屈服,23°C | ASTMD638 | 5.0 | % |
| elongation | 断裂,23°C | ASTMD638 | 330 | % |
| Bending modulus | 23°C | ASTMD790 | 1800 | Mpa |
| Bending modulus | 23°C,4.00mm | ISO178 | 1800 | Mpa |
| bending strength | 23°C,4.00mm | ISO178 | 63.0 | Mpa |
| bending strength | 屈服,23°C | ASTMD790 | 66.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ASTMD648 | 74.0 | °C |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 74.0 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 64.0 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 65.0 | °C |
| specific heat | 60°C | | 1340 | J/kg/°C |
| specific heat | 240°C | | 2050 | J/kg/°C |
| specific heat | 导热系数(23°C) | | 0.19 | W/m/K |
| Vicat softening temperature | | ASTMD15252 | 88.0 | °C |
| Vicat softening temperature | -- | ISO306/A | 88.0 | °C |
| Vicat softening temperature | -- | ISO306/B | 79.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation factor | 23°C,1kHz | ASTMD150 | 5.6E-03 | |
| Dissipation factor | 23°C,10kHz | ASTMD150 | 0.012 | |
| Dissipation factor | 23°C,100kHz | ASTMD150 | 0.016 | |
| Dissipation factor | 23°C,1MHz | ASTMD150 | 0.018 | |
| Dielectric strength | 23°C | ASTMD149 | 16 | KV/mm |
| Dielectric constant | 23°C,1kHz | ASTMD150 | 2.70 | |
| Dielectric constant | 23°C,10kHz | ASTMD150 | 2.70 | |
| Dielectric constant | 23°C,100kHz | ASTMD150 | 2.60 | |
| Dielectric constant | 23°C,1MHz | ASTMD150 | 2.50 | |
| Arc resistance | | ASTMD495 | 66.0 | sec |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Multi axis Instrumented Impact Energy | -40°C,能量到力量峰值 | ISO6603-2 | 16.0 | J |
| Multi axis Instrumented Impact Energy | 23°C,能量到力量峰值 | ISO6603-2 | 14.0 | J |
| Impact strength of cantilever beam gap | -40°C | ISO180 | 7.4 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180 | 130 | kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ASTMD4218 | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ASTMD4218 | NoBreak | |
| Impact strength of cantilever beam gap | -40°C | ASTMD256 | 64 | J/m |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | NoBreak | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R计秤,23°C | ASTMD785 | 105 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| UL flame retardant rating | 3.2mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.