Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 流动 : 3.20 mm | ASTM D955 | 0.50 到 0.70 | % |
| Shrinkage rate | 3.20 mm | ISO 2577 | 0.50 到 0.70 | % |
| Melt flow rate | 300°C/1.2 kg | ASTM D1238, ISO 1133 | 27 | g/10 min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending modulus | 23°C | ASTM D790, ISO 178 | 2250 | Mpa |
| bending strength | 23°C | ASTM D790, ISO 178 | 100 | Mpa |
| Tensile strength | 23°C | ASTM D638, ISO 527-2 | 59.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 3.18 mm | ASTM D648, ISO 75-2/A | 122 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R 级, 23°C | ASTM D785 | 122 | |
| Rockwell hardness | R 计秤, 23°C | ISO 2039-2 | 122 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.0 mm | UL 94 | V-2 | |
| UL flame retardant rating | 3.0 mm | UL 94 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.