Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.02 | kg·cm/cm(J/M)ft·lb/in |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.25 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | | ISO 294-4 | 0.9/0.9 | % |
| Water absorption rate | | ISO 62 | 0.6 | % |
| melting point | | ISO 11357-3 | 179 | °C |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Yield modulus | | ISO 527-1/-2 | 4 | % |
| Tensile yield strength | | ISO 527-1/-2 | 47 | Mpa |
| Shore hardness | | ISO 868 | 77 | D |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 3C | KJ/m |
| Charpy Notched Impact Strength | -40℃ | ISO 179/1eA | 3C | KJ/m |
| elongation | 断裂 | ISO 527-1/-2 | ＞200 | % |
| Rockwell hardness | | ASTM D785 | 110 | |
| Rockwell hardness | | ISO 2039-2 | 105 | R |
| Bending modulus | | ASTM D412/ISO 527 | 14500 | kg/cm²(MPa)[Lb/in²] |
| Bending modulus | | ISO 178 | 1500 | Mpa |
| bending strength | | ISO 178 | 60 | Mpa |
| bending strength | | ASTM D790/ISO 178 | 560 | kg/cm²(MPa)[Lb/in²] |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 5 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Coefficient of linear expansion | | ISO 11359-2 | 1.3 | |
| Hot deformation temperature | -，0.45Mpa | ISO 75-2 | 95 | °C |
| Hot deformation temperature | -，1.8Mpa | ISO 75-2 | 45 | °C |
| melting point | | | 176-180 | ℃（℉） |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 10 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | ASTM D257/IEC 60093 | 10^15 | Ω.cm |
| Volume resistivity | | IEC 60093 | 10 | Ω.cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.