Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt flow rate | 190°C/2.16 kg | ISO 1133 | 0.40 | g/10 min |
| Butyl acrylate component | | 内部方法 | 17.0 | wt% |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature | | 内部方法 | 96.0 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film thickness - tested 2 | | | 100 | µm |
| Tensile stress | MD : 断裂, 100 µm, 吹塑薄膜 | ISO 527-3 | 29.0 | Mpa |
| Tensile stress | TD : 断裂, 100 µm, 吹塑薄膜 | ISO 527-3 | 30.0 | Mpa |
| elongation | MD : 断裂, 100 µm, 吹塑薄膜 | ISO 527-3 | 750 | % |
| elongation | TD : 断裂, 100 µm, 吹塑薄膜 | ISO 527-3 | 850 | % |
| Falling hammer impact | 100 µm, 吹塑薄膜 | ISO 7765-1 | > 1400 | g |
| Elmondov tear strength | MD : 100 µm, 吹塑薄膜 | ISO 6383-2 | 3.6 | N |
| Elmondov tear strength | TD : 100 µm, 吹塑薄膜 | ISO 6383-2 | 3.9 | N |
| squeeze | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Temperature | | | 180 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.