Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.20 | % |
| density | 23°C | ISO1183 | 1.22 | g/cm³ |
| Melt volume flow rate | 270°C/5.0kg | ISO1133 | 20.0 | cm3/10min |
| Shrinkage rate | TD | ISO2577 | 0.60to0.80 | % |
| Shrinkage rate | MD | ISO2577 | 0.60to0.80 | % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.50 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2/50 | 59.0 | Mpa |
| Tensile stress | 断裂,23°C | ISO527-2/50 | 64.0 | Mpa |
| Tensile strain | 屈服,23°C | ISO527-2/50 | 5.5 | % |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | 100 | % |
| Bending modulus | 23°C | ISO178 | 2350 | Mpa |
| Bending stress | 23°C | ISO178 | 88.0 | Mpa |
| Bending stress | 3.5%Strain,23°C | ISO178 | 71.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 131 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 109 | °C |
| Vicat softening temperature | | ISO306/B120 | 142 | °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO11359-2 | 7E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO11359-2 | 8E-05 | cm/cm/°C |
| ThermalConductivity | 23°C | ISO8302 | 0.20 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+16 | ohms |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Leakage Trace Index | 解决方案A | IEC60112 | 375 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | -30°C | ISO7391 | 10 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO7391 | 60 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.