Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt flow rate | 220°C/10.0 kg | ASTM D1238 | 21 | g/10 min |
| Shrinkage rate - flow | 23°C, 3.20 mm, 注塑 | ASTM D955 | 0.40 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Elongation rate 4 | 屈服, 23°C, 3.20 mm, 注塑 | ASTM D638 | > 5.0 | % |
| Elongation rate 4 | 断裂, 23°C, 3.20 mm, 注塑 | ASTM D638 | 15 | % |
| Tensile modulus | 23°C, 3.20 mm, 注塑 | ASTM D638 | 2050 | Mpa |
| Bending modulus | 23°C, 3.20 mm, 注塑 | ASTM D790 | 2250 | Mpa |
| bending strength | 23°C, 3.20 mm, 注塑 | ASTM D790 | 71.0 | Mpa |
| Tensile strength | 屈服, 23°C, 3.20 mm, 注塑 | ASTM D638 | 48.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTM D15257 | 89.0 | °C |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 6.40 mm, 注塑 | ASTM D648 | 81.0 | °C |
| RTI | | UL 746 | 50.0 | °C |
| RTI Imp | | UL 746 | 50.0 | °C |
| RTI Elec | | UL 746 | 50.0 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 80 到 90 | °C |
| Processing (melt) temperature | | | 190 到 220 | °C |
| Mold temperature | | | 40 到 60 | °C |
| drying time | | | 2.0 到 4.0 | hr |
| Temperature at the rear of the barrel | | | 180 到 200 | °C |
| Temperature in the middle of the barrel | | | 190 到 210 | °C |
| Temperature at the front of the material cylinder | | | 200 到 220 | °C |
| Spray nozzle temperature | | | 190 到 220 | °C |
| Back pressure | | | 29.4 到 58.8 | Mpa |
| Screw speed | | | 30 到 60 | rpm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R 级, 23°C, 注塑 | ASTM D785 | 107 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 注塑 | ASTM D1003 | 2.0 | % |
| transmissivity | 3200 µm, 注塑 | ASTM D1003 | 90.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB | |
| UL flame retardant rating | 3.0 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.