Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.18 | |
| Molding shrinkage rate | | ASTM D955 | 0.2-0.6 | % |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.3 | % |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 14.5 | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | | ASTM D1238 | 14.5 | g/10 min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| tensile strength | | ASTM D638/ISO 527 | 670 | kg/cm²(MPa)[Lb/in²] |
| Rockwell hardness | | ASTM D785 | 69 | |
| Bending modulus | | ASTM D790/ISO 178 | 31000 | kg/cm²(MPa)[Lb/in²] |
| Bending modulus | | ASTM D790 | 3040 | Mpa |
| bending strength | | ASTM D790 | 0.961 | Mpa |
| bending strength | | ASTM D790/ISO 178 | 980 | kg/cm²(MPa)[Lb/in²] |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 1.2 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Glass transition temperature | | ASTM E1356 | 92.0 | °C |
| Vicat softening temperature | | ASTM D1525 | 88.0 | °C |
| Hot deformation temperature | | ASTM D648/ISO 75 | 77 | ℃（℉） |
| vicat softening point | | ASTM D1525/ISO R306 | 88 | ℃（℉） |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Transmittance | | ASTM D1003 | 92.0 | % |
| Light transmittance | | ASTM D1003/ISO 13468 | 92 | % |
| Refractive index | | ASTM D542/ISO 489 | 1.49 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.