Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 9.0 | g/10min |
| Content of comonomer 3 | | 内部方法 | 6.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | 屈服,模压成型 | ASTMD638,ISO527-2 | 7.89 | Mpa |
| Tensile strength | 断裂,模压成型 | ASTMD638,ISO527-2 | 17.2 | Mpa |
| elongation | 断裂,模压成型 | ASTMD638,ISO527-2 | 630 | % |
| Tensile yield strength | Compression Molded | MPa | ASTM D-638 | 7.89 |
| Tensile yield strength | Compression Molded | MPa | ISO 527-2 | 7.89 |
| Tensile fracture strength | Compression Molded | MPa | ASTM D-638 | |
| Tensile fracture strength | Compression Molded | MPa | ISO 527-2 | |
| Tensile strain at break | Compression Molded | % | ASTM D-638 | |
| Tensile strain at break | Compression Molded | % | ISO 527-2 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTMD1525,ISO306 | 83.9 | °C |
| Melting temperature (DSC) | | 内部方法 | 101 | °C |
| vicat softening point | | ℃ | ASTM D-1525 | 83.9 |
| vicat softening point | | ℃ | ISO 306 | 83.9 |
| Melting temperature | | ℃ | Internal Method | 101 |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Initial sealing temperature 4 | | 内部方法 | 92.8 | °C |
| Water vapor permeability | 38°C,90%RH | DIN53122/2 | 0.40 | g·mm/m²/atm/24hr |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Temperature | | ℃ | | 260-290 |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Sealing starting temperature | | ℃ | Internal Method | 92.8 |
| Water vapor transmission rate | 38℃，90% RH | g·mm/m | DIN 53122/2 | |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 190℃/2.16kg | g/10min | ASTM D-1238 | |
| Melt index | 190℃/2.16kg | g/10min | ISO 1133 | |
| Monomer content | | % | Internal Method | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.