Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 10.8 | kg·cm/cm(J/M)ft·lb/in |
| Molding shrinkage rate | | ASTM D955 | 0.3-0.7 | % |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.2 | % |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 12 | g/10min |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 10 | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption | | | 0.2 | % |
| Disassembly rate | | | 1.569 | |
| Melting temperature range for pipeline extrusion | | | 220-240 | °C |
| Melting temperature range for injection molding | | | 220-270 | °C |
| Temperature range of mold | | | 40-80 | °C |
| Melt index | 200/21 6 | | 12 | |
| Melt index | 220/10 | | 10 | |
| Shrinkage rate | | | 0.3-0.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy impact strength | +23/-40℃ | | 18/18 | KJ/m |
| Tensile modulus of elasticity | | | 3800 | Mpa |
| Tensile creep modulus | 1000h 伸长率＜＝0.5%+23℃ | | 2800 | Mpa |
| elongation | | | 3 | % |
| Rockwell hardness | | ASTM D785 | 83 | |
| Rockwell hardness | | | 83 | M |
| Yield stress under maximum stress | | | 125 | Mpa |
| Fracture stress | | | 75 | Mpa |
| Charpy Notched Impact Strength | 23℃ | | 2 | KJ/m |
| Impact strength of cantilever beam gap | 23℃ | | 2 | KJ/m |
| Ball pressure hardness | | | 165 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Maximum operating temperature | | | 85 | °C |
| Conductivity | | | 0.17 | W/K.m |
| Hot deformation temperature | 0.45MPa(HDT B) | | 102 | °C |
| Hot deformation temperature | 1.8MPa(HDT A) | | 98 | °C |
| melting point | | | 85 | ℃（℉） |
| vicat softening point | | ASTM D1525/ISO R306 | 106 | ℃（℉） |
| vicat softening point | | | 106 | °C |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 7 | mm/mm.℃ |
| Linear expansion coefficient | 纵向(23-80)℃ | | 7 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | K20/P20 | | 95 | KV/mm |
| Volume resistance | | | 10 | Ω.cm |
| Relative Arc Track Index CTI Test Solution | 试验溶液B | | CTI 200M | |
| Relative Arc Track Index CTI Test Solution | 试验溶液A/CTIM | | CTI 425 | |
| Surface resistance | | | 10 | Ω |
| Loss angle | 100Hz/1MHz | | 0.004/0.007 | |
| Dielectric constant | 100Hz/1MHz | | 3/2.7 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.