| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 200°C/5.0kg | ISO1133 | 1.8 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | 断裂 | ISO527-2/5 | 50.0 | Mpa |
| Tensile strain | 断裂 | ISO527-2/5 | <3.0 | % |
| Bending modulus 2 | | ISO178 | 3400 | Mpa |
| Bending stress 2 | | ISO178 | 109 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 81.0 | °C |
| Vicat softening temperature | | ISO306/B | 102 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M计秤,23°C | ISO2039-2 | 75 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 2000µm | ISO14782 | 0.30 | % |
| transmissivity | 2000µm | ISO13468 | 90.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.