Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 1.0 | g/10min |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 1.0 | g/10min |
| IonType | | | Sodium | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength 2 | Yield,23°C,CompressionMolded | ASTMD638 | 3.10 | Mpa |
| Tensile strength | 断裂,23°C | ASTMD638 | 18.6 | Mpa |
| Tensile stress | 断裂,23°C | ISO527-2 | 18.6 | Mpa |
| elongation | 断裂,23°C | ASTMD638 | 560 | % |
| Tensile strain | 断裂,23°C | ISO527-2 | 560 | % |
| Bending modulus | 23°C | ASTMD790 | 30.3 | Mpa |
| Wear resistance - NBSIdex | | ASTMD1630 | 61.0 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTMD1525 | 47.0 | °C |
| Vicat softening temperature | | ISO306 | 47.0 | °C |
| Peak melting temperature | | ASTMD3418 | 70.0 | °C |
| Melting temperature (DSC) | | ISO3146 | 70.0 | °C |
| FreezingPoint | -- | ASTMD3418 | 38 | °C |
| FreezingPoint | -- | ISO3146 | 38 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile impact strength | 23°C | ASTMD1822 | 1270 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | 邵氏D | ASTMD2240 | 36 | |
| Shore hardness | 邵氏D | ISO868 | 36 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 6350µm | ASTMD1003 | 27 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.