Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ISO1183 | 1.35 | g/cm³ |
| Water absorption rate 2 | 饱和,23°C,2.00mm | ISO62 | 6.2 | % |
| Water absorption rate 2 | 平衡,23°C,2.00mm,50%RH | ISO62 | 1.8 | % |
| Shrinkage rate 2 | TD | ISO294-4 | 1.0 | % |
| Shrinkage rate 2 | MD | ISO294-4 | 0.20 | % |
| MediumDensity2 | | | 1.31 | g/cm³ |
| SpecificHeatCapacity of Melt2 | | | 2200 | J/kg/°C |
| ThermalConductivityofMelt2 | | | 0.23 | W/m/K |
| Top out temperature | | | 210 | °C |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress 3 | 断裂 | ISO527-2 | 160 | Mpa |
| Tensile strain 2 | 断裂 | ISO527-2 | 3.3 | % |
| Tensile modulus 2 | | ISO527-2 | 9500 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 210 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 206 | °C |
| Vicat softening temperature | | ISO306/B50 | 210 | °C |
| Linear coefficient of thermal expansion | MD2 | ISO11359-2 | 3E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD2 | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| Melting temperature 5 | | ISO11357-3 | 220 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam gap 4 | -30°C | ISO179/1eA | 10 | kJ/m² |
| Impact strength of simply supported beam gap 4 | 23°C | ISO179/1eA | 14 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating 2 | 1.5mm | IEC60695-11-10,-20 | HB | |
| Burning rate 6 | 1.00mm | ISO3795 | <100 | mm/min |
| FMVSS flammability | | FMVSS302 | B | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.