Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 2781/JIS K7311 | 1.20. | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hardness A | | ASTM D2240/ISO 868 | 92±2 | Shore A |
| Tensile strength | | ASTM D412 | ＞35.0 | Mpa |
| Abrasion resistance | | ASTM D1044 | 40 | mg |
| 300% modulus | | ASTM D412 | ＞12.0 | Mpa |
| 100% modulus | | ASTM D412/ISO 527 | ＞7.0 | Mpa/Psi |
| 300% modulus | | ASTM D412/ISO 527 | ＞12.0 | Mpa/Psi |
| Tensile strength | | ASTM D412/ISO 527 | ＞35.0 | Mpa/Psi |
| tear strength | | ASTM D624/ISO 34 | ＞100 | n/mm² |
| Resilience | | ASTM D1054 | 45 | % |
| 100% modulus | | ASTM D412 | ＞7.0 | Mpa |
| hardness | shore A | ASTM D2240 | 92±2 | |
| hardness | shore D | ASTM D2240 | 无 | |
| tear strength | | ASTM D624 | ＞100 | N/mm |
| Permanent compression deformation | (70℃×24h) | ASTM D395 | 45 | % |
| Permanent compression deformation | (23℃×70h) | ASTM D395 | 33 | % |
| elongation | | ASTM D412 | ＞400 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Glass transition temperature Tg | | ASTM D3417 | ＜-70 | °C |
| Low temperature softening temperature | | ASTM D1053 | -44 | °C |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Processing temperature | | | 190-205 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.